牌號 410C21
對應(yīng)標準 BS 3100-1991
一般工程用鑄鋼件
Specification for Steel castings for general engineering purposes
歸類 鑄鋼
性能 耐腐蝕
標簽 不銹鋼鑄鋼
410C21 化學元素成分含量(%)
成分 C Si Mn P S Cr Ni Cu ①
最小值 - - - - - 11.5 - -
最大值 0.15 1 1 0.04 0.04 13.5 1 0.3
①殘余元素
410C21 機械性能
熱處理或狀態(tài)
抗拉強度
σb
Mpa 		屈服點
σs
Mpa 		斷后伸長率或延伸率
δ
%
AH+T或OQ+T(T at 750°C max) ≥540 ≥370 ≥15
A=for anneal by heating to a temperature above the AC3 and cool in the furnace
N=for normalize by heating to a temperature above the AC3 and cool in still air
OQ=for quench into oil from a temperature above the AC3
WQ=for quench into water from a temperature above the AC3
AH=for air harden by heating to a temperature above the AC3 and cool in air at a rate fast enough to produce a hardened microstructure
T=for temper by heating to a temperature below AC1
ST=for solution treat by heating to temperature high enough to dissolve and any intermetallic phases followed by a rapid cool.
1 近似對照表 耐蝕鑄鋼（不銹鋼鑄件）
中國 中國臺灣 日本 韓國 美國 國際標準組織 德國 法國 俄羅斯 瑞典 英國
GB ISC CNS JIS KS ASTM UNS ISO DIN EN/DIN W-Nr. NF EN/NF GOST SS14 BS EN/BS
ZG15Cr12 C54100 SCS 1 SCS 1X SSC 1 CA15 J91150 GX12Cr12 GX12Cr12 1.4011 Z12C13M 15Х13Л 2302 410C21
2 近似對照表 耐蝕鑄鋼（不銹鋼鑄件）
中國 日本 美國 德國 法國 俄羅斯 英國
GB JIS ASTM DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG1Cr13 SUS1 CA15 G-X8Cr14
X15Cr13 		1.4008
1.4024 		Z12C13M 15Х13Л 410C21
3 近似對照表 耐熱鑄鋼和耐熱合金鑄件
中國 日本 美國 德國 法國 俄羅斯 英國
GB JIS ASTM UNS DIN EN/DIN W-Nr. NF EN/NF GOST BS EN/BS
ZG1Cr13 SCS1 CA15 J91150 G-X7Cr13
G-X10Cr13 		1.4001
1.4006 		Z12C13M 15Х13Л 410C21
注：數(shù)據(jù)僅供參考！如有疑問丘苗，請?zhí)顚?我要糾錯"私爷！
© 2024 材數(shù)庫
版權(quán)說明：
⑴ 本網(wǎng)站的所有內(nèi)容（包括但不限于文字撬彭、圖片砾淌、音頻洋训、視頻等）均受到版權(quán)保護洋访，版權(quán)歸本網(wǎng)站所有器钟；
⑵ 未經(jīng)授權(quán)，禁止以任何形式轉(zhuǎn)載绽媒、復制蚕冬、傳播或用于其他商業(yè)用途；
⑶ 如需使用本網(wǎng)站內(nèi)容是辕，請?zhí)崆矮@得授權(quán)囤热。